Add to the silicone at a ratio of 2% to achieve vibrant colors.
Color pigments can be added to both addition platinum cured and condensation tin-cured rubbers.
The pigments are non-toxic and are suitable for use in rubber that will contact both food and skin.
Small amounts can be added to creat tones, the more pigment color strong.
Multiple colors can be mixed to create custom colors.
Add to the silicone at a ratio of 2% to achieve vibrant colors.
Color pigments can be added to both addition platinum cured and condensation tin-cured rubbers.
The pigments are non-toxic and are suitable for use in rubber that will contact both food and skin.
Small amounts can be added to creat tones, the more pigment color strong.
Multiple colors can be mixed to create custom colors.
£3.30Original price was: £3.30.£3.10Current price is: £3.10.
RTV2 Condensation type Silicone tin catalyst Recommended for general mold work Silicone
Base Color: White Curing Agent: Transparent/BlueMix ratio: 100:2 Pot life: 30-40 mins Curing time: 4-6 hrs Hardness: 15-28 shore A
Product is skin and food safe
For the platinum Catalyst system this can be added either liquid, however for the silicone tin catalyst system it should be added to base paste not the catalyst.
Use: to soften silicone molds. Only a small quantity is required.
Adding above 5% will start retarding the reaction giving a longer pot life and cure time
Tin/Condensation Cured Silicone- guide
1ml added to 100ml base paste hardness reduced by 10%
3ml added to 100ml base paste hardness reduced by 30%
5ml added to 100ml base paste hardness reduced by 50%
Platinum/Addition Cured Silicone
5ml added to 100ml base paste hardness reduced by 9%
10ml added to 100ml base paste hardness reduced by 18%
15ml added to 100ml base paste hardness reduced by 25%
Silicone putty is new silicone compounds (platinum catalyst) that can be easiy mixed and applied by hand to a variety of usage . It has a pot life of about 5-20 mins with a cure time of about 30-60 mins at room temperature.Shrinkage is low and cured rubber is exceptionally strong (very high tensile strength) .They also resist cure inhibition.
suitable for DIY mols, Foot and Hoof impressions.
Thermal Conductive Two-Component RTV Silicone Elastomer for Electronics Potting
Two-component room temperature cure potting compound with mix ratio of 1: 1, curing time can be accelerated by heating up, features with good flow ability and flame resistance. It's suitable for encapsulating of LED displayers, power module and electronics components, etc.
RTV2 Condensation type Silicone tin catalyst Recommended for general mold work Silicone
Base Color: White Curing Agent: Transparent/BlueMix ratio: 100:2 Pot life: 30-40 mins Curing time: 4-6 hrs Hardness: 15-28 shore A
Silicone Putty is new silicone compounds (platinum catalyst) that can be easily mixed and applied by hand and it is mixed in equal amounts (1A:1B) by volume/weight, it has a pot life of about 2-3 minute with a cure time of about 5-8 min at room temperature (73°F/23°C). Shrinkage is low and cured rubber is exceptionally strong (very high tensile strength), They also resist cure inhibition. It is also FOOD SAFE and can be used for culinary applications.
RTV2 Condensation type tin catalyst silicone for Statue and sculpture use Mix Ratio: 100: 2 Hardness: 25-30 Shore
Silicone Base: White Curing Agent: Clear/Blue/Yellow/Orage/Green